LG Chem ABS HP171

Kufotokozera Kwachidule:

Utomoni wa ABS, granule ya pulasitiki yoyera, mapulasitiki opangidwa ndi zinthu, polystyrene copolymer, LG Chem raw material, Korea ABS resin

Tumizani imelo kwa ife Tsitsani ngati PDF

Tsatanetsatane wa Zamalonda

Mawonekedwe

Kulimba kwambiri, kunyezimira kwambiri, kusalala bwino kwa pamwamba, mphamvu ya makina yolinganizidwa, kukonza kosavuta kwa jakisoni, kuyenda kosasunthika kwa madzi osungunuka, utoto wabwino, kuchepa pang'ono kwa mapangidwe.

Mapulogalamu

Amagwiritsidwa ntchito kwambiri pa zipangizo zapakhomo, zoseweretsa, ma CD okongoletsera, zofunikira za tsiku ndi tsiku, zipolopolo za zida zaofesi ndi mitundu yonse ya zinthu zopangira jekeseni.

Kulongedza

Chikwama cha pulasitiki chopangidwa ndi pepala cha 25kg

LG Chem ABS HP171
Katundu	Njira Yoyesera	Chigawo	Kufotokozera	Mtengo Wamba
Katundu Wathupi
Kuchulukana	ASTM D792	g/cm³	1.04~1.06	1.05
Kuumba Kuchepa	ASTM D955	%	0.4~0.7	0.5
Kuchuluka kwa Kuthamanga kwa Madzi (220°C/10kg)	ASTM D1238	g/10min	20~30	25
Madontho a Madontho pa Pulasitiki	Muyezo Wamkati	/10kg	≤16	1
Granule Yaikulu ndi Yaing'ono	Muyezo Wamkati	g/kg	≤5	0.00
Katundu wa Makina
Kupsinjika Maganizo Pakukula	ASTM D638	MPa	≥45	48.8
Kutalikirana kwa Kulimba pa Nthawi Yopuma	ASTM D638	%	≥7	36
Mphamvu Yosinthasintha	ASTM D790	MPa	≥65	73
Modulus Yosinthasintha	ASTM D790	MPa	≥2100	2296
Mphamvu ya Izod Impact (23°C, yodulidwa)	ASTM D256	kJ/m²	≥18	24
Kulimba kwa Rockwell (R-Scale)	ASTM D785	-	≥105	108
Katundu wa Kutentha
Kutentha Kofewa kwa Vicat	ASTM D1525	°C	≥90	95
Kutentha Kochepa (1.8MPa)	ASTM D648	°C	≥80	85
Kutha kuyaka (1.6mm)	UL94	-	HB	HB
Katundu Wokonza
Kutentha Koyenera Kopangira Ma Molding	Zothandiza	°C	200~240	220
Kutentha Koyenera kwa Nkhungu	Zothandiza	°C	40~60	50